SPEC scans from: /share1/USAXS_data/2021-01/01_29_Coakley1/01_29_Coakley1.dat

spec file: /share1/USAXS_data/2021-01/01_29_Coakley1/01_29_Coakley1.dat
#2: documentation_run() #3: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059980999999999, 9.062481]', per_step='None') #4: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463, 8.7476]', per_step='None') #5: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.003800000000005, 47.003800000000005]', per_step='None') #6: SAXS(detectors=['saxs_det'], num=1) #7: WAXS(detectors=['waxs_det'], num=1) #8: documentation_run() #9: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060018, 9.062518]', per_step='None') #10: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463, 8.7476]', per_step='None') #11: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.524100000000004, 47.524100000000004]', per_step='None') #12: SAXS(detectors=['saxs_det'], num=1) #13: WAXS(detectors=['waxs_det'], num=1) #14: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060018999999999, 9.062519]', per_step='None') #15: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463653, 8.747665300000001]', per_step='None') #16: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.3308, 47.3308]', per_step='None') #17: Flyscan(pos_X=0.0, pos_Y=0.0, thickness=1.0, scan_title='HeaterBlank_26C_96min') #18: documentation_run() #19: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059999999999999, 9.0625]', per_step='None') #20: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463563, 8.747656300000001]', per_step='None') #21: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.267900000000004, 47.267900000000004]', per_step='None') #22: SAXS(detectors=['saxs_det'], num=1) #23: WAXS(detectors=['waxs_det'], num=1) #24: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060000999999998, 9.062501]', per_step='None') #25: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463563, 8.747656300000001]', per_step='None') #26: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.246100000000006, 47.246100000000006]', per_step='None') #27: Flyscan(pos_X=0.0, pos_Y=0.0, thickness=1.0, scan_title='HeaterBlank_26C_103min') #28: documentation_run() #29: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060014999999998, 9.062515]', per_step='None') #30: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463695, 8.7476695]', per_step='None') #31: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.017900000000004, 47.017900000000004]', per_step='None') #32: SAXS(detectors=['saxs_det'], num=1) #33: WAXS(detectors=['waxs_det'], num=1) #34: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.06003, 9.06253]', per_step='None') #35: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463695, 8.7476695]', per_step='None') #36: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 41.9367, 46.9367]', per_step='None') #37: Flyscan(pos_X=0.0, pos_Y=0.0, thickness=1.0, scan_title='Ni115') #38: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060007999999998, 9.062508]', per_step='None') #39: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746331300000001, 8.747631300000002]', per_step='None') #40: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.173700000000004, 47.173700000000004]', per_step='None') #41: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059997999999998, 9.062498]', per_step='None') #42: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746331300000001, 8.747631300000002]', per_step='None') #43: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.150600000000004, 47.150600000000004]', per_step='None') #44: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_30C_0min') #45: SAXS(detectors=['saxs_det'], num=1) #46: WAXS(detectors=['waxs_det'], num=1) #47: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059997, 9.062497]', per_step='None') #48: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463312, 8.7476312]', per_step='None') #49: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.1944, 47.1944]', per_step='None') #50: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_31C_0min') #51: SAXS(detectors=['saxs_det'], num=1) #52: WAXS(detectors=['waxs_det'], num=1) #53: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_251C_0min') #54: SAXS(detectors=['saxs_det'], num=1) #55: WAXS(detectors=['waxs_det'], num=1) #56: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_250C_0min') #57: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060008999999999, 9.062509]', per_step='None') #58: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463925, 8.747692500000001]', per_step='None') #59: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 41.827600000000004, 46.827600000000004]', per_step='None') #60: SAXS(detectors=['saxs_det'], num=1) #61: WAXS(detectors=['waxs_det'], num=1) #62: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_0min') #63: SAXS(detectors=['saxs_det'], num=1) #64: WAXS(detectors=['waxs_det'], num=1) #65: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_4min') #66: SAXS(detectors=['saxs_det'], num=1) #67: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060004, 9.062504]', per_step='None') #68: WAXS(detectors=['waxs_det'], num=1) #69: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_9min') #70: SAXS(detectors=['saxs_det'], num=1) #71: WAXS(detectors=['waxs_det'], num=1) #72: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_13min') #73: SAXS(detectors=['saxs_det'], num=1) #74: WAXS(detectors=['waxs_det'], num=1) #75: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059957999999998, 9.062458]', per_step='None') #76: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746366400000001, 8.747666400000002]', per_step='None') #77: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 41.9212, 46.9212]', per_step='None') #78: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_17min') #79: SAXS(detectors=['saxs_det'], num=1) #80: WAXS(detectors=['waxs_det'], num=1) #81: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_22min') #82: SAXS(detectors=['saxs_det'], num=1) #83: WAXS(detectors=['waxs_det'], num=1) #84: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_26min') #85: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060007999999998, 9.062508]', per_step='None') #86: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746430400000001, 8.747730400000002]', per_step='None') #87: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 41.552600000000005, 46.552600000000005]', per_step='None') #88: SAXS(detectors=['saxs_det'], num=1) #89: WAXS(detectors=['waxs_det'], num=1) #90: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_31min') #91: SAXS(detectors=['saxs_det'], num=1) #92: WAXS(detectors=['waxs_det'], num=1) #93: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_36min') #94: SAXS(detectors=['saxs_det'], num=1) #95: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059999, 9.062499]', per_step='None') #96: WAXS(detectors=['waxs_det'], num=1) #97: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_40min') #98: SAXS(detectors=['saxs_det'], num=1) #99: WAXS(detectors=['waxs_det'], num=1) #100: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_45min') #101: SAXS(detectors=['saxs_det'], num=1) #102: WAXS(detectors=['waxs_det'], num=1) #103: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059989999999999, 9.06249]', per_step='None') #104: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746388600000001, 8.747688600000002]', per_step='None') #105: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 41.8108, 46.8108]', per_step='None') #106: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_49min') #107: SAXS(detectors=['saxs_det'], num=1) #108: WAXS(detectors=['waxs_det'], num=1) #109: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_54min') #110: SAXS(detectors=['saxs_det'], num=1) #111: WAXS(detectors=['waxs_det'], num=1) #112: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_58min') #113: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060039999999999, 9.06254]', per_step='None') #114: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464379, 8.7477379]', per_step='None') #115: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 41.6297, 46.6297]', per_step='None') #116: SAXS(detectors=['saxs_det'], num=1) #117: WAXS(detectors=['waxs_det'], num=1) #118: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_63min') #119: SAXS(detectors=['saxs_det'], num=1) #120: WAXS(detectors=['waxs_det'], num=1) #121: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_67min') #122: SAXS(detectors=['saxs_det'], num=1) #123: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060006, 9.062506]', per_step='None') #124: WAXS(detectors=['waxs_det'], num=1) #125: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_72min') #126: SAXS(detectors=['saxs_det'], num=1) #127: WAXS(detectors=['waxs_det'], num=1) #128: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_76min') #129: SAXS(detectors=['saxs_det'], num=1) #130: WAXS(detectors=['waxs_det'], num=1) #131: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059978999999998, 9.062479]', per_step='None') #132: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463931, 8.747693100000001]', per_step='None') #133: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 41.9773, 46.9773]', per_step='None') #134: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_81min') #135: SAXS(detectors=['saxs_det'], num=1) #136: WAXS(detectors=['waxs_det'], num=1) #137: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_86min') #138: SAXS(detectors=['saxs_det'], num=1) #139: WAXS(detectors=['waxs_det'], num=1) #140: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_90min') #141: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060016999999998, 9.062517]', per_step='None') #142: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463861, 8.747686100000001]', per_step='None') #143: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.1132, 47.1132]', per_step='None') #144: SAXS(detectors=['saxs_det'], num=1) #145: WAXS(detectors=['waxs_det'], num=1) #146: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_95min') #147: SAXS(detectors=['saxs_det'], num=1) #148: WAXS(detectors=['waxs_det'], num=1) #149: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_99min') #150: SAXS(detectors=['saxs_det'], num=1) #151: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060018999999999, 9.062519]', per_step='None') #152: WAXS(detectors=['waxs_det'], num=1) #153: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_104min') #154: SAXS(detectors=['saxs_det'], num=1) #155: WAXS(detectors=['waxs_det'], num=1) #156: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_108min') #157: SAXS(detectors=['saxs_det'], num=1) #158: WAXS(detectors=['waxs_det'], num=1) #159: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059961999999999, 9.062462]', per_step='None') #160: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463926, 8.7476926]', per_step='None') #161: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.1604, 47.1604]', per_step='None') #162: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_112min') #163: SAXS(detectors=['saxs_det'], num=1) #164: WAXS(detectors=['waxs_det'], num=1) #165: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_117min') #166: SAXS(detectors=['saxs_det'], num=1) #167: WAXS(detectors=['waxs_det'], num=1) #168: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_772C_122min') #169: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060009999999998, 9.06251]', per_step='None') #170: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463739, 8.7476739]', per_step='None') #171: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.3662, 47.3662]', per_step='None') #172: SAXS(detectors=['saxs_det'], num=1) #173: WAXS(detectors=['waxs_det'], num=1) #174: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_250C_0min') #175: SAXS(detectors=['saxs_det'], num=1) #176: WAXS(detectors=['waxs_det'], num=1) #177: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_0min') #178: SAXS(detectors=['saxs_det'], num=1) #179: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060000999999998, 9.062501]', per_step='None') #180: WAXS(detectors=['waxs_det'], num=1) #181: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_5min') #182: SAXS(detectors=['saxs_det'], num=1) #183: WAXS(detectors=['waxs_det'], num=1) #184: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_9min') #185: SAXS(detectors=['saxs_det'], num=1) #186: WAXS(detectors=['waxs_det'], num=1) #187: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060006, 9.062506]', per_step='None') #188: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746345100000001, 8.747645100000002]', per_step='None') #189: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.6045, 47.6045]', per_step='None') #190: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_13min') #191: SAXS(detectors=['saxs_det'], num=1) #192: WAXS(detectors=['waxs_det'], num=1) #193: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_18min') #194: SAXS(detectors=['saxs_det'], num=1) #195: WAXS(detectors=['waxs_det'], num=1) #196: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_22min') #197: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060042, 9.062542]', per_step='None') #198: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464043, 8.7477043]', per_step='None') #199: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.4437, 47.4437]', per_step='None') #200: SAXS(detectors=['saxs_det'], num=1) #201: WAXS(detectors=['waxs_det'], num=1) #202: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_27min') #203: SAXS(detectors=['saxs_det'], num=1) #204: WAXS(detectors=['waxs_det'], num=1) #205: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_32min') #206: SAXS(detectors=['saxs_det'], num=1) #207: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059999999999999, 9.0625]', per_step='None') #208: WAXS(detectors=['waxs_det'], num=1) #209: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_36min') #210: SAXS(detectors=['saxs_det'], num=1) #211: WAXS(detectors=['waxs_det'], num=1) #212: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_41min') #213: SAXS(detectors=['saxs_det'], num=1) #214: WAXS(detectors=['waxs_det'], num=1) #215: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059975999999999, 9.062476]', per_step='None') #216: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463458, 8.7476458]', per_step='None') #217: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.842400000000005, 47.842400000000005]', per_step='None') #218: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_45min') #219: SAXS(detectors=['saxs_det'], num=1) #220: WAXS(detectors=['waxs_det'], num=1) #221: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_50min') #222: SAXS(detectors=['saxs_det'], num=1) #223: WAXS(detectors=['waxs_det'], num=1) #224: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_54min') #225: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060016999999998, 9.062517]', per_step='None') #226: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463801, 8.7476801]', per_step='None') #227: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.7898, 47.7898]', per_step='None') #228: SAXS(detectors=['saxs_det'], num=1) #229: WAXS(detectors=['waxs_det'], num=1) #230: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_59min') #231: SAXS(detectors=['saxs_det'], num=1) #232: WAXS(detectors=['waxs_det'], num=1) #233: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_63min') #234: SAXS(detectors=['saxs_det'], num=1) #235: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060011, 9.062511]', per_step='None') #236: WAXS(detectors=['waxs_det'], num=1) #237: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_68min') #238: SAXS(detectors=['saxs_det'], num=1) #239: WAXS(detectors=['waxs_det'], num=1) #240: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_72min') #241: SAXS(detectors=['saxs_det'], num=1) #242: WAXS(detectors=['waxs_det'], num=1) #243: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060007999999998, 9.062508]', per_step='None') #244: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463689, 8.7476689]', per_step='None') #245: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.9545, 47.9545]', per_step='None') #246: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_77min') #247: SAXS(detectors=['saxs_det'], num=1) #248: WAXS(detectors=['waxs_det'], num=1) #249: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_82min') #250: SAXS(detectors=['saxs_det'], num=1) #251: WAXS(detectors=['waxs_det'], num=1) #252: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_86min') #253: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060011999999999, 9.062512]', per_step='None') #254: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463697, 8.747669700000001]', per_step='None') #255: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.108900000000006, 48.108900000000006]', per_step='None') #256: SAXS(detectors=['saxs_det'], num=1) #257: WAXS(detectors=['waxs_det'], num=1) #258: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_91min') #259: SAXS(detectors=['saxs_det'], num=1) #260: WAXS(detectors=['waxs_det'], num=1) #261: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_95min') #262: SAXS(detectors=['saxs_det'], num=1) #263: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060051, 9.062551000000001]', per_step='None') #264: WAXS(detectors=['waxs_det'], num=1) #265: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_100min') #266: SAXS(detectors=['saxs_det'], num=1) #267: WAXS(detectors=['waxs_det'], num=1) #268: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_104min') #269: SAXS(detectors=['saxs_det'], num=1) #270: WAXS(detectors=['waxs_det'], num=1) #271: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059999, 9.062499]', per_step='None') #272: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464393, 8.747739300000001]', per_step='None') #273: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 42.9694, 47.9694]', per_step='None') #274: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_108min') #275: SAXS(detectors=['saxs_det'], num=1) #276: WAXS(detectors=['waxs_det'], num=1) #277: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_113min') #278: SAXS(detectors=['saxs_det'], num=1) #279: WAXS(detectors=['waxs_det'], num=1) #280: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_118min') #281: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060035, 9.062535]', per_step='None') #282: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463861, 8.747686100000001]', per_step='None') #283: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.3647, 48.3647]', per_step='None') #284: SAXS(detectors=['saxs_det'], num=1) #285: WAXS(detectors=['waxs_det'], num=1) #286: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_800C_123min') #287: SAXS(detectors=['saxs_det'], num=1) #288: WAXS(detectors=['waxs_det'], num=1) #289: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_249C_0min') #290: SAXS(detectors=['saxs_det'], num=1) #291: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060042999999999, 9.062543]', per_step='None') #292: WAXS(detectors=['waxs_det'], num=1) #293: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_0min') #294: SAXS(detectors=['saxs_det'], num=1) #295: WAXS(detectors=['waxs_det'], num=1) #296: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_4min') #297: SAXS(detectors=['saxs_det'], num=1) #298: WAXS(detectors=['waxs_det'], num=1) #299: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059990999999998, 9.062491]', per_step='None') #300: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464461, 8.7477461]', per_step='None') #301: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.1689, 48.1689]', per_step='None') #302: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_9min') #303: SAXS(detectors=['saxs_det'], num=1) #304: WAXS(detectors=['waxs_det'], num=1) #305: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_14min') #306: SAXS(detectors=['saxs_det'], num=1) #307: WAXS(detectors=['waxs_det'], num=1) #308: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_18min') #309: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060025, 9.062525]', per_step='None') #310: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463795, 8.7476795]', per_step='None') #311: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.571200000000005, 48.571200000000005]', per_step='None') #312: SAXS(detectors=['saxs_det'], num=1) #313: WAXS(detectors=['waxs_det'], num=1) #314: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_23min') #315: SAXS(detectors=['saxs_det'], num=1) #316: WAXS(detectors=['waxs_det'], num=1) #317: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_27min') #318: SAXS(detectors=['saxs_det'], num=1) #319: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060039999999999, 9.06254]', per_step='None') #320: WAXS(detectors=['waxs_det'], num=1) #321: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_32min') #322: SAXS(detectors=['saxs_det'], num=1) #323: WAXS(detectors=['waxs_det'], num=1) #324: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_36min') #325: SAXS(detectors=['saxs_det'], num=1) #326: WAXS(detectors=['waxs_det'], num=1) #327: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059976999999998, 9.062477]', per_step='None') #328: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464505, 8.7477505]', per_step='None') #329: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.2873, 48.2873]', per_step='None') #330: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_40min') #331: SAXS(detectors=['saxs_det'], num=1) #332: WAXS(detectors=['waxs_det'], num=1) #333: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_45min') #334: SAXS(detectors=['saxs_det'], num=1) #335: WAXS(detectors=['waxs_det'], num=1) #336: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_50min') #337: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060023, 9.062523]', per_step='None') #338: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463841, 8.7476841]', per_step='None') #339: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.7245, 48.7245]', per_step='None') #340: SAXS(detectors=['saxs_det'], num=1) #341: WAXS(detectors=['waxs_det'], num=1) #342: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_55min') #343: SAXS(detectors=['saxs_det'], num=1) #344: WAXS(detectors=['waxs_det'], num=1) #345: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_59min') #346: SAXS(detectors=['saxs_det'], num=1) #347: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060001999999999, 9.062502]', per_step='None') #348: WAXS(detectors=['waxs_det'], num=1) #349: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_63min') #350: SAXS(detectors=['saxs_det'], num=1) #351: WAXS(detectors=['waxs_det'], num=1) #352: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_68min') #353: SAXS(detectors=['saxs_det'], num=1) #354: WAXS(detectors=['waxs_det'], num=1) #355: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060007999999998, 9.062508]', per_step='None') #356: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746434, 8.747734000000001]', per_step='None') #357: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.5056, 48.5056]', per_step='None') #358: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_72min') #359: SAXS(detectors=['saxs_det'], num=1) #360: WAXS(detectors=['waxs_det'], num=1) #361: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_77min') #362: SAXS(detectors=['saxs_det'], num=1) #363: WAXS(detectors=['waxs_det'], num=1) #364: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_81min') #365: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060023, 9.062523]', per_step='None') #366: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464022, 8.7477022]', per_step='None') #367: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.7322, 48.7322]', per_step='None') #368: SAXS(detectors=['saxs_det'], num=1) #369: WAXS(detectors=['waxs_det'], num=1) #370: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_86min') #371: SAXS(detectors=['saxs_det'], num=1) #372: WAXS(detectors=['waxs_det'], num=1) #373: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_91min') #374: SAXS(detectors=['saxs_det'], num=1) #375: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060023999999999, 9.062524]', per_step='None') #376: WAXS(detectors=['waxs_det'], num=1) #377: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_95min') #378: SAXS(detectors=['saxs_det'], num=1) #379: WAXS(detectors=['waxs_det'], num=1) #380: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_100min') #381: SAXS(detectors=['saxs_det'], num=1) #382: WAXS(detectors=['waxs_det'], num=1) #383: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059947, 9.062447]', per_step='None') #384: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464341, 8.7477341]', per_step='None') #385: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.6171, 48.6171]', per_step='None') #386: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_104min') #387: SAXS(detectors=['saxs_det'], num=1) #388: WAXS(detectors=['waxs_det'], num=1) #389: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_109min') #390: SAXS(detectors=['saxs_det'], num=1) #391: WAXS(detectors=['waxs_det'], num=1) #392: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_113min') #393: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060037, 9.062537]', per_step='None') #394: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464251, 8.7477251]', per_step='None') #395: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.7685, 48.7685]', per_step='None') #396: SAXS(detectors=['saxs_det'], num=1) #397: WAXS(detectors=['waxs_det'], num=1) #398: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_118min') #399: SAXS(detectors=['saxs_det'], num=1) #400: WAXS(detectors=['waxs_det'], num=1) #401: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_829C_122min') #402: SAXS(detectors=['saxs_det'], num=1) #403: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060011999999999, 9.062512]', per_step='None') #404: WAXS(detectors=['waxs_det'], num=1) #405: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_249C_0min') #406: SAXS(detectors=['saxs_det'], num=1) #407: WAXS(detectors=['waxs_det'], num=1) #408: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_0min') #409: SAXS(detectors=['saxs_det'], num=1) #410: WAXS(detectors=['waxs_det'], num=1) #411: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059935999999999, 9.062436]', per_step='None') #412: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746421, 8.747721]', per_step='None') #413: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.8218, 48.8218]', per_step='None') #414: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_4min') #415: SAXS(detectors=['saxs_det'], num=1) #416: WAXS(detectors=['waxs_det'], num=1) #417: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_9min') #418: SAXS(detectors=['saxs_det'], num=1) #419: WAXS(detectors=['waxs_det'], num=1) #420: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_14min') #421: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060033999999998, 9.062534]', per_step='None') #422: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464296, 8.747729600000001]', per_step='None') #423: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.8671, 48.8671]', per_step='None') #424: SAXS(detectors=['saxs_det'], num=1) #425: WAXS(detectors=['waxs_det'], num=1) #426: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_19min') #427: SAXS(detectors=['saxs_det'], num=1) #428: WAXS(detectors=['waxs_det'], num=1) #429: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_23min') #430: SAXS(detectors=['saxs_det'], num=1) #431: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060007999999998, 9.062508]', per_step='None') #432: WAXS(detectors=['waxs_det'], num=1) #433: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_27min') #434: SAXS(detectors=['saxs_det'], num=1) #435: WAXS(detectors=['waxs_det'], num=1) #436: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_32min') #437: SAXS(detectors=['saxs_det'], num=1) #438: WAXS(detectors=['waxs_det'], num=1) #439: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059992, 9.062492]', per_step='None') #440: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464294, 8.7477294]', per_step='None') #441: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.8964, 48.8964]', per_step='None') #442: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_36min') #443: SAXS(detectors=['saxs_det'], num=1) #444: WAXS(detectors=['waxs_det'], num=1) #445: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_41min') #446: SAXS(detectors=['saxs_det'], num=1) #447: WAXS(detectors=['waxs_det'], num=1) #448: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_45min') #449: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060027999999999, 9.062528]', per_step='None') #450: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746441500000001, 8.747741500000002]', per_step='None') #451: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.8361, 48.8361]', per_step='None') #452: SAXS(detectors=['saxs_det'], num=1) #453: WAXS(detectors=['waxs_det'], num=1) #454: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_50min') #455: SAXS(detectors=['saxs_det'], num=1) #456: WAXS(detectors=['waxs_det'], num=1) #457: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_55min') #458: SAXS(detectors=['saxs_det'], num=1) #459: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060013999999999, 9.062514]', per_step='None') #460: WAXS(detectors=['waxs_det'], num=1) #461: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_59min') #462: SAXS(detectors=['saxs_det'], num=1) #463: WAXS(detectors=['waxs_det'], num=1) #464: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_63min') #465: SAXS(detectors=['saxs_det'], num=1) #466: WAXS(detectors=['waxs_det'], num=1) #467: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059980999999999, 9.062481]', per_step='None') #468: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464293, 8.747729300000001]', per_step='None') #469: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.947300000000006, 48.947300000000006]', per_step='None') #470: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_68min') #471: SAXS(detectors=['saxs_det'], num=1) #472: WAXS(detectors=['waxs_det'], num=1) #473: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_73min') #474: SAXS(detectors=['saxs_det'], num=1) #475: WAXS(detectors=['waxs_det'], num=1) #476: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_77min') #477: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060023, 9.062523]', per_step='None') #478: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464452, 8.7477452]', per_step='None') #479: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.8958, 48.8958]', per_step='None') #480: SAXS(detectors=['saxs_det'], num=1) #481: WAXS(detectors=['waxs_det'], num=1) #482: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_82min') #483: SAXS(detectors=['saxs_det'], num=1) #484: WAXS(detectors=['waxs_det'], num=1) #485: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_86min') #486: SAXS(detectors=['saxs_det'], num=1) #487: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060042, 9.062542]', per_step='None') #488: WAXS(detectors=['waxs_det'], num=1) #489: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_91min') #490: SAXS(detectors=['saxs_det'], num=1) #491: WAXS(detectors=['waxs_det'], num=1) #492: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_95min') #493: SAXS(detectors=['saxs_det'], num=1) #494: WAXS(detectors=['waxs_det'], num=1) #495: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060018, 9.062518]', per_step='None') #496: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464554, 8.7477554]', per_step='None') #497: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.8915, 48.8915]', per_step='None') #498: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_100min') #499: SAXS(detectors=['saxs_det'], num=1) #500: WAXS(detectors=['waxs_det'], num=1) #501: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_105min') #502: SAXS(detectors=['saxs_det'], num=1) #503: WAXS(detectors=['waxs_det'], num=1) #504: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_109min') #505: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060025999999999, 9.062526]', per_step='None') #506: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464314, 8.747731400000001]', per_step='None') #507: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.0422, 49.0422]', per_step='None') #508: SAXS(detectors=['saxs_det'], num=1) #509: WAXS(detectors=['waxs_det'], num=1) #510: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_114min') #511: SAXS(detectors=['saxs_det'], num=1) #512: WAXS(detectors=['waxs_det'], num=1) #513: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_118min') #514: SAXS(detectors=['saxs_det'], num=1) #515: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060011, 9.062511]', per_step='None') #516: WAXS(detectors=['waxs_det'], num=1) #517: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_859C_123min') #518: SAXS(detectors=['saxs_det'], num=1) #519: WAXS(detectors=['waxs_det'], num=1) #520: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_249C_0min') #521: SAXS(detectors=['saxs_det'], num=1) #522: WAXS(detectors=['waxs_det'], num=1) #523: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059982999999999, 9.062483]', per_step='None') #524: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464479, 8.7477479]', per_step='None') #525: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.9319, 48.9319]', per_step='None') #526: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_888C_0min') #527: SAXS(detectors=['saxs_det'], num=1) #528: WAXS(detectors=['waxs_det'], num=1) #529: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_5min') #530: SAXS(detectors=['saxs_det'], num=1) #531: WAXS(detectors=['waxs_det'], num=1) #532: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_9min') #533: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060011, 9.062511]', per_step='None') #534: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464115, 8.747711500000001]', per_step='None') #535: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.118900000000004, 49.118900000000004]', per_step='None') #536: SAXS(detectors=['saxs_det'], num=1) #537: WAXS(detectors=['waxs_det'], num=1) #538: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_14min') #539: SAXS(detectors=['saxs_det'], num=1) #540: WAXS(detectors=['waxs_det'], num=1) #541: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_19min') #542: SAXS(detectors=['saxs_det'], num=1) #543: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060009999999998, 9.06251]', per_step='None') #544: WAXS(detectors=['waxs_det'], num=1) #545: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_23min') #546: SAXS(detectors=['saxs_det'], num=1) #547: WAXS(detectors=['waxs_det'], num=1) #548: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_27min') #549: SAXS(detectors=['saxs_det'], num=1) #550: WAXS(detectors=['waxs_det'], num=1) #551: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059988999999998, 9.062489]', per_step='None') #552: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746453500000001, 8.747753500000002]', per_step='None') #553: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.900000000000006, 48.900000000000006]', per_step='None') #554: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_32min') #555: SAXS(detectors=['saxs_det'], num=1) #556: WAXS(detectors=['waxs_det'], num=1) #557: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_37min') #558: SAXS(detectors=['saxs_det'], num=1) #559: WAXS(detectors=['waxs_det'], num=1) #560: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_41min') #561: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060011999999999, 9.062512]', per_step='None') #562: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746411700000001, 8.747711700000002]', per_step='None') #563: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.1755, 49.1755]', per_step='None') #564: SAXS(detectors=['saxs_det'], num=1) #565: WAXS(detectors=['waxs_det'], num=1) #566: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_46min') #567: SAXS(detectors=['saxs_det'], num=1) #568: WAXS(detectors=['waxs_det'], num=1) #569: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_50min') #570: SAXS(detectors=['saxs_det'], num=1) #571: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060027999999999, 9.062528]', per_step='None') #572: WAXS(detectors=['waxs_det'], num=1) #573: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_55min') #574: SAXS(detectors=['saxs_det'], num=1) #575: WAXS(detectors=['waxs_det'], num=1) #576: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_59min') #577: SAXS(detectors=['saxs_det'], num=1) #578: WAXS(detectors=['waxs_det'], num=1) #579: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059980999999999, 9.062481]', per_step='None') #580: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746481000000001, 8.747781000000002]', per_step='None') #581: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.831500000000005, 48.831500000000005]', per_step='None') #582: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_63min') #583: SAXS(detectors=['saxs_det'], num=1) #584: WAXS(detectors=['waxs_det'], num=1) #585: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_68min') #586: SAXS(detectors=['saxs_det'], num=1) #587: WAXS(detectors=['waxs_det'], num=1) #588: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_73min') #589: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060025, 9.062525]', per_step='None') #590: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746420800000001, 8.747720800000002]', per_step='None') #591: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.1495, 49.1495]', per_step='None') #592: SAXS(detectors=['saxs_det'], num=1) #593: WAXS(detectors=['waxs_det'], num=1) #594: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_78min') #595: SAXS(detectors=['saxs_det'], num=1) #596: WAXS(detectors=['waxs_det'], num=1) #597: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_82min') #598: SAXS(detectors=['saxs_det'], num=1) #599: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060061, 9.062561]', per_step='None') #600: WAXS(detectors=['waxs_det'], num=1) #601: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_87min') #602: SAXS(detectors=['saxs_det'], num=1) #603: WAXS(detectors=['waxs_det'], num=1) #604: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_91min') #605: SAXS(detectors=['saxs_det'], num=1) #606: WAXS(detectors=['waxs_det'], num=1) #607: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.059999999999999, 9.0625]', per_step='None') #608: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7465092, 8.7478092]', per_step='None') #609: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.7777, 48.7777]', per_step='None') #610: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_95min') #611: SAXS(detectors=['saxs_det'], num=1) #612: WAXS(detectors=['waxs_det'], num=1) #613: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_100min') #614: SAXS(detectors=['saxs_det'], num=1) #615: WAXS(detectors=['waxs_det'], num=1) #616: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_105min') #617: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060037999999999, 9.062538]', per_step='None') #618: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746422500000001, 8.747722500000002]', per_step='None') #619: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.244, 49.244]', per_step='None') #620: SAXS(detectors=['saxs_det'], num=1) #621: WAXS(detectors=['waxs_det'], num=1) #622: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_109min') #623: SAXS(detectors=['saxs_det'], num=1) #624: WAXS(detectors=['waxs_det'], num=1) #625: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_114min') #626: SAXS(detectors=['saxs_det'], num=1) #627: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060025, 9.062525]', per_step='None') #628: WAXS(detectors=['waxs_det'], num=1) #629: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_118min') #630: SAXS(detectors=['saxs_det'], num=1) #631: WAXS(detectors=['waxs_det'], num=1) #632: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_889C_123min') #633: SAXS(detectors=['saxs_det'], num=1) #634: WAXS(detectors=['waxs_det'], num=1) #635: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060011999999999, 9.062512]', per_step='None') #636: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746479200000001, 8.747779200000002]', per_step='None') #637: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.893100000000004, 48.893100000000004]', per_step='None') #638: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_249C_0min') #639: SAXS(detectors=['saxs_det'], num=1) #640: WAXS(detectors=['waxs_det'], num=1) #641: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_0min') #642: SAXS(detectors=['saxs_det'], num=1) #643: WAXS(detectors=['waxs_det'], num=1) #644: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_4min') #645: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060042, 9.062542]', per_step='None') #646: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746413800000001, 8.747713800000001]', per_step='None') #647: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.408100000000005, 49.408100000000005]', per_step='None') #648: SAXS(detectors=['saxs_det'], num=1) #649: WAXS(detectors=['waxs_det'], num=1) #650: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_9min') #651: SAXS(detectors=['saxs_det'], num=1) #652: WAXS(detectors=['waxs_det'], num=1) #653: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_14min') #654: SAXS(detectors=['saxs_det'], num=1) #655: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060061, 9.062561]', per_step='None') #656: WAXS(detectors=['waxs_det'], num=1) #657: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_18min') #658: SAXS(detectors=['saxs_det'], num=1) #659: WAXS(detectors=['waxs_det'], num=1) #660: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_22min') #661: SAXS(detectors=['saxs_det'], num=1) #662: WAXS(detectors=['waxs_det'], num=1) #663: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060011, 9.062511]', per_step='None') #664: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746547, 8.747847]', per_step='None') #665: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.162, 49.162]', per_step='None') #666: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_27min') #667: SAXS(detectors=['saxs_det'], num=1) #668: WAXS(detectors=['waxs_det'], num=1) #669: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_32min') #670: SAXS(detectors=['saxs_det'], num=1) #671: WAXS(detectors=['waxs_det'], num=1) #672: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_36min') #673: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060028999999998, 9.062529]', per_step='None') #674: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464809, 8.7477809]', per_step='None') #675: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.3301, 49.3301]', per_step='None') #676: SAXS(detectors=['saxs_det'], num=1) #677: WAXS(detectors=['waxs_det'], num=1) #678: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_41min') #679: SAXS(detectors=['saxs_det'], num=1) #680: WAXS(detectors=['waxs_det'], num=1) #681: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_45min') #682: SAXS(detectors=['saxs_det'], num=1) #683: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060049999999999, 9.06255]', per_step='None') #684: WAXS(detectors=['waxs_det'], num=1) #685: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_50min') #686: SAXS(detectors=['saxs_det'], num=1) #687: WAXS(detectors=['waxs_det'], num=1) #688: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_54min') #689: SAXS(detectors=['saxs_det'], num=1) #690: WAXS(detectors=['waxs_det'], num=1) #691: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060025999999999, 9.062526]', per_step='None') #692: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7465653, 8.7478653]', per_step='None') #693: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.806200000000004, 48.806200000000004]', per_step='None') #694: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_59min') #695: SAXS(detectors=['saxs_det'], num=1) #696: WAXS(detectors=['waxs_det'], num=1) #697: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_64min') #698: SAXS(detectors=['saxs_det'], num=1) #699: WAXS(detectors=['waxs_det'], num=1) #700: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_68min') #701: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060047999999998, 9.062548]', per_step='None') #702: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746471600000001, 8.747771600000002]', per_step='None') #703: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.9227, 48.9227]', per_step='None') #704: SAXS(detectors=['saxs_det'], num=1) #705: WAXS(detectors=['waxs_det'], num=1) #706: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_73min') #707: SAXS(detectors=['saxs_det'], num=1) #708: WAXS(detectors=['waxs_det'], num=1) #709: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_77min') #710: SAXS(detectors=['saxs_det'], num=1) #711: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060038999999998, 9.062539]', per_step='None') #712: WAXS(detectors=['waxs_det'], num=1) #713: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_82min') #714: SAXS(detectors=['saxs_det'], num=1) #715: WAXS(detectors=['waxs_det'], num=1) #716: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_86min') #717: SAXS(detectors=['saxs_det'], num=1) #718: WAXS(detectors=['waxs_det'], num=1) #719: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060025, 9.062525]', per_step='None') #720: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464986, 8.747798600000001]', per_step='None') #721: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.8191, 48.8191]', per_step='None') #722: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_90min') #723: SAXS(detectors=['saxs_det'], num=1) #724: WAXS(detectors=['waxs_det'], num=1) #725: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_95min') #726: SAXS(detectors=['saxs_det'], num=1) #727: WAXS(detectors=['waxs_det'], num=1) #728: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_100min') #729: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060014999999998, 9.062515]', per_step='None') #730: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746435, 8.747735]', per_step='None') #731: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.159, 49.159]', per_step='None') #732: SAXS(detectors=['saxs_det'], num=1) #733: WAXS(detectors=['waxs_det'], num=1) #734: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_105min') #735: SAXS(detectors=['saxs_det'], num=1) #736: WAXS(detectors=['waxs_det'], num=1) #737: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_109min') #738: SAXS(detectors=['saxs_det'], num=1) #739: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060054, 9.062554]', per_step='None') #740: WAXS(detectors=['waxs_det'], num=1) #741: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_113min') #742: SAXS(detectors=['saxs_det'], num=1) #743: WAXS(detectors=['waxs_det'], num=1) #744: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_118min') #745: SAXS(detectors=['saxs_det'], num=1) #746: WAXS(detectors=['waxs_det'], num=1) #747: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060023, 9.062523]', per_step='None') #748: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7465236, 8.7478236]', per_step='None') #749: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.0443, 49.0443]', per_step='None') #750: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_950C_122min') #751: SAXS(detectors=['saxs_det'], num=1) #752: WAXS(detectors=['waxs_det'], num=1) #753: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_249C_0min') #754: SAXS(detectors=['saxs_det'], num=1) #755: WAXS(detectors=['waxs_det'], num=1) #756: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1015C_0min') #757: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060028999999998, 9.062529]', per_step='None') #758: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746449700000001, 8.747749700000002]', per_step='None') #759: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.336800000000004, 49.336800000000004]', per_step='None') #760: SAXS(detectors=['saxs_det'], num=1) #761: WAXS(detectors=['waxs_det'], num=1) #762: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1015C_5min') #763: SAXS(detectors=['saxs_det'], num=1) #764: WAXS(detectors=['waxs_det'], num=1) #765: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1015C_9min') #766: SAXS(detectors=['saxs_det'], num=1) #767: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060018, 9.062518]', per_step='None') #768: WAXS(detectors=['waxs_det'], num=1) #769: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1015C_14min') #770: SAXS(detectors=['saxs_det'], num=1) #771: WAXS(detectors=['waxs_det'], num=1) #772: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1015C_18min') #773: SAXS(detectors=['saxs_det'], num=1) #774: WAXS(detectors=['waxs_det'], num=1) #775: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060009999999998, 9.06251]', per_step='None') #776: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7465168, 8.7478168]', per_step='None') #777: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.9065, 48.9065]', per_step='None') #778: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_249C_0min') #779: SAXS(detectors=['saxs_det'], num=1) #780: WAXS(detectors=['waxs_det'], num=1) #781: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1083C_0min') #782: SAXS(detectors=['saxs_det'], num=1) #783: WAXS(detectors=['waxs_det'], num=1) #784: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1083C_4min') #785: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060045999999998, 9.062546]', per_step='None') #786: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746404, 8.747704]', per_step='None') #787: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.239200000000004, 49.239200000000004]', per_step='None') #788: SAXS(detectors=['saxs_det'], num=1) #789: WAXS(detectors=['waxs_det'], num=1) #790: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1083C_9min') #791: SAXS(detectors=['saxs_det'], num=1) #792: WAXS(detectors=['waxs_det'], num=1) #793: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1083C_14min') #794: SAXS(detectors=['saxs_det'], num=1) #795: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060035, 9.062535]', per_step='None') #796: WAXS(detectors=['waxs_det'], num=1) #797: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1083C_18min') #798: SAXS(detectors=['saxs_det'], num=1) #799: WAXS(detectors=['waxs_det'], num=1) #800: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_250C_0min') #801: SAXS(detectors=['saxs_det'], num=1) #802: WAXS(detectors=['waxs_det'], num=1) #803: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060008999999999, 9.062509]', per_step='None') #804: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7465467, 8.7478467]', per_step='None') #805: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.0554, 49.0554]', per_step='None') #806: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1155C_0min') #807: SAXS(detectors=['saxs_det'], num=1) #808: WAXS(detectors=['waxs_det'], num=1) #809: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1155C_5min') #810: SAXS(detectors=['saxs_det'], num=1) #811: WAXS(detectors=['waxs_det'], num=1) #812: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1155C_9min') #813: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060064999999998, 9.062565]', per_step='None') #814: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7465281, 8.747828100000001]', per_step='None') #815: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.8958, 48.8958]', per_step='None') #816: SAXS(detectors=['saxs_det'], num=1) #817: WAXS(detectors=['waxs_det'], num=1) #818: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1155C_14min') #819: SAXS(detectors=['saxs_det'], num=1) #820: WAXS(detectors=['waxs_det'], num=1) #821: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_1155C_19min') #822: SAXS(detectors=['saxs_det'], num=1) #823: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060061, 9.062561]', per_step='None') #824: WAXS(detectors=['waxs_det'], num=1) #825: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_250C_0min') #826: SAXS(detectors=['saxs_det'], num=1) #827: WAXS(detectors=['waxs_det'], num=1) #828: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_43C_4min') #829: SAXS(detectors=['saxs_det'], num=1) #830: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060025, 9.062525]', per_step='None') #831: WAXS(detectors=['waxs_det'], num=1) #832: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_34C_9min') #833: SAXS(detectors=['saxs_det'], num=1) #834: WAXS(detectors=['waxs_det'], num=1) #835: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_33C_13min') #836: SAXS(detectors=['saxs_det'], num=1) #837: WAXS(detectors=['waxs_det'], num=1) #838: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060018999999999, 9.062519]', per_step='None') #839: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746593500000001, 8.747893500000002]', per_step='None') #840: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.555, 48.555]', per_step='None') #841: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_33C_18min') #842: SAXS(detectors=['saxs_det'], num=1) #843: WAXS(detectors=['waxs_det'], num=1) #844: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_33C_22min') #845: SAXS(detectors=['saxs_det'], num=1) #846: WAXS(detectors=['waxs_det'], num=1) #847: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_33C_27min') #848: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060037, 9.062537]', per_step='None') #849: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7463437, 8.747643700000001]', per_step='None') #850: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.1019, 49.1019]', per_step='None') #851: SAXS(detectors=['saxs_det'], num=1) #852: WAXS(detectors=['waxs_det'], num=1) #853: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_33C_32min') #854: SAXS(detectors=['saxs_det'], num=1) #855: WAXS(detectors=['waxs_det'], num=1) #856: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_33C_36min') #857: SAXS(detectors=['saxs_det'], num=1) #858: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060051, 9.062551000000001]', per_step='None') #859: WAXS(detectors=['waxs_det'], num=1) #860: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_33C_41min') #861: SAXS(detectors=['saxs_det'], num=1) #862: WAXS(detectors=['waxs_det'], num=1) #863: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_45min') #864: SAXS(detectors=['saxs_det'], num=1) #865: WAXS(detectors=['waxs_det'], num=1) #866: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060059999999998, 9.06256]', per_step='None') #867: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746406200000001, 8.747706200000001]', per_step='None') #868: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.1428, 49.1428]', per_step='None') #869: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_49min') #870: SAXS(detectors=['saxs_det'], num=1) #871: WAXS(detectors=['waxs_det'], num=1) #872: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_54min') #873: SAXS(detectors=['saxs_det'], num=1) #874: WAXS(detectors=['waxs_det'], num=1) #875: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_59min') #876: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060051999999999, 9.062552]', per_step='None') #877: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.746389200000001, 8.747689200000002]', per_step='None') #878: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.4211, 49.4211]', per_step='None') #879: SAXS(detectors=['saxs_det'], num=1) #880: WAXS(detectors=['waxs_det'], num=1) #881: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_63min') #882: SAXS(detectors=['saxs_det'], num=1) #883: WAXS(detectors=['waxs_det'], num=1) #884: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_68min') #885: SAXS(detectors=['saxs_det'], num=1) #886: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060071999999998, 9.062572]', per_step='None') #887: WAXS(detectors=['waxs_det'], num=1) #888: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_72min') #889: SAXS(detectors=['saxs_det'], num=1) #890: WAXS(detectors=['waxs_det'], num=1) #891: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_77min') #892: SAXS(detectors=['saxs_det'], num=1) #893: WAXS(detectors=['waxs_det'], num=1) #894: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.06003, 9.06253]', per_step='None') #895: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464429, 8.7477429]', per_step='None') #896: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.253, 49.253]', per_step='None') #897: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_81min') #898: SAXS(detectors=['saxs_det'], num=1) #899: WAXS(detectors=['waxs_det'], num=1) #900: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_86min') #901: SAXS(detectors=['saxs_det'], num=1) #902: WAXS(detectors=['waxs_det'], num=1) #903: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_90min') #904: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060057999999998, 9.062558]', per_step='None') #905: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464119, 8.7477119]', per_step='None') #906: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.4087, 49.4087]', per_step='None') #907: SAXS(detectors=['saxs_det'], num=1) #908: WAXS(detectors=['waxs_det'], num=1) #909: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_32C_95min') #910: SAXS(detectors=['saxs_det'], num=1) #911: WAXS(detectors=['waxs_det'], num=1) #912: Flyscan(pos_X=0, pos_Y=0, thickness=0.06, scan_title='Ni115_31C_100min') #913: SAXS(detectors=['saxs_det'], num=1) #914: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060026999999998, 9.062527]', per_step='None') #915: WAXS(detectors=['waxs_det'], num=1) #916: documentation_run() #917: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060011, 9.062511]', per_step='None') #918: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464011, 8.7477011]', per_step='None') #919: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 44.363600000000005, 49.363600000000005]', per_step='None') #920: SAXS(detectors=['saxs_det'], num=1) #921: WAXS(detectors=['waxs_det'], num=1) #922: tune_mr(detectors=('I0_USAXS',), num=31, args='['m_stage_r', 9.060042999999999, 9.062543]', per_step='None') #923: tune_ar(detectors=('PD_USAXS',), num=35, args='['a_stage_r', 8.7464011, 8.7477011]', per_step='None') #924: tune_a2rp(detectors=('PD_USAXS',), num=31, args='['a_stage_r2p', 43.9795, 48.9795]', per_step='None') #925: Flyscan(pos_X=0.0, pos_Y=0.0, thickness=1.0, scan_title='HeaterBlank')